熱門關鍵詞：
-
鋁焊絲
牌號相當GB相當AWSCuAlCrFeMnSiZnMgTi特性和用途供應規格技術文檔S301SAI1070ER1070≤0.04≥99.5≤0.3≤0.03≤0.3塑性好、耐蝕。純鋁氣焊、氬弧焊用。盤裝Φ1.0mm Φ1.2mmΦ1.6mm Φ2.0mmΦ2.4mm直條Φ1.6mm Φ2.0mmΦ2.4mm Φ3.0mmΦ4.0mm Φ5.0mmΦ6.0mm長度1000mmER4043(S311)SAI4043ER4043≤0.30余量≤0.60≤0.054.5~6.0≤0.10≤0.05≤0.20抗裂性好、通用性大。鋁合金氣焊、氬弧焊用。不宜用于鋁鎂合金。ER4047BAl88Si BAlSi-4≤0.30余量≤0.80≤0.1511.0~13.0≤0.20≤0.10適用于鑄鋁、2000系列以及鋁鎂硅系列鋁合金的焊接。ER4047FBAl88SiBAlS-4≤0.30余量≤0.80≤0.1511.0~13.0≤0.20≤0.10適用于鑄鋁、2000系列以及鋁鎂硅系列鋁合金的焊接。ER5183SAI5183ER5183≤0.10余量0.05~0.25≤0.400.50~1.0≤0.40≤0.254.3~5.2≤0.15耐蝕、強度高。鋁合金氬弧焊用。ER5356SAI5356ER5356≤0.10余量0.05~0.20≤0.400.05~0.20≤0.25≤0.104.5~5.50.06~0.20耐蝕、強度高、通用性大。鋁合金氬弧焊用。ER5556 (S331)SAI5556ER5556≤0.10余量0.05~0.20≤0.400.50~1.0≤0.25≤0.254.7~5.50.05~0.20
粉末硬度化學成分（重量%）典型用途CCrSiWFeMoNiCoMnBStellite 1482.4030.501.0012.503.001.003.00Bal0.25閥座、軸承、刀口等Stellite 3482.3030.501.0012.503.002.50Bal針閥座、閥座、軋鋼導向輥Stellite 6381.1529.001.104.003.001.003.00Bal0.50發動機氣門、高溫高壓閥門、渦輪機葉片Stellite 12421.4029.501.458.253.001.003.00Bal1.00高溫高壓閥門、鋸齒、螺旋推桿等Stellite 20522.4532.501.0017.53.001.003.00Bal0.50軸承套筒、耐磨板Stellite 21280.2527.502.000.152.005.502.50Bal1.00渦輪機葉片、各種流體閥、閥座等Stellite 25冷硬0.1020.001.0015.003.001.0010.00Bal1.50沖壓、擠壓模具Stellite 31310.5025.501.007.502.0010.50Bal1.00擠壓模、燃氣渦輪葉片Stellite 156431.6028.001.154.500.501.003.00Bal1.00高溫高壓閥門、熱鍛模Stellite 157500.1022.001.604.503.000.303.00Bal0.302.40摩托車閥頂端Stellite 158400.7526.001.905.503.000.503.00Bal0.100.70高溫高壓閥門、鋸齒、螺旋推桿等Stellite 158W411.3031.001.505.504.502.00Bal0.70閥座、高溫高壓閥門等Stellite F371.7525.501.1012.003.000.6022.50Bal0.50內燃機進排氣閥Tribaloy X-400.8525.000.307.501.0010.00Bal0.30沖壓、擠壓模具燃氣渦輪葉片Tribaloy 400530.088.502.601.5028.501.50Bal用于高溫強腐蝕介質中的閘閥、擠塑器Tribaloy 800530.0818.003.401.5028.501.50Bal用于高溫強腐蝕介質中的閘閥、擠塑器Tribaloy 9000.0818.002.70Mo:232.5016.00Bal閥座、密封圈、高溫熱軋輥stellite SF6410.7019.002.307.503.0013.50Bal1.001.70發動機氣門、高溫高壓閥門Stellite SF12431.0019.002.809.003.0013.00Bal1.001.80高溫高壓閥門、熱剪切刀刃等Stellite 706401.1029.002.00Mo:52.002.00Bal發動機氣門、高溫高壓閥門Stellite 712471.9029.002.00Mo:8.52.002.00Bal高溫高壓閥門、螺旋推桿粉末硬度化學成分（重量%）典型用途Haystellite 16050%Deloro60+50%WC（鑄造cast）混料機葉片、刮板、風機葉片Haystellite 26065%Deloro60+35%WC（鑄造cast）混料機葉片、刮板、風機葉片Haystellite 36085%Deloro60+15%WC（鑄造cast）混料機葉片、刮板、風機葉片Haystellite 46040%Deloro60+60%WC（鑄造cast）混料機葉片、刮板、風機葉片Haystellite 76070%Deloro60+30%WC（鑄造cast）混料機葉片、刮板、風機葉片Haystellite 86060%Deloro60+40%WC（鑄造cast）混料機葉片、刮板、風機葉片NiWC 256075%Ni60+25%WC混料機葉片、刮板、風機葉片NiWC 356065%Ni60+35%WC風機葉片、螺旋輸入器等JK112110(HV)12%Co/88%WC球閥、壓縮機軸、泵密封圈等JK1171010(HV)17%Co/83%WC閥門、導向桿、壓紙輥等JK1201000(HV)10%Co/4%Cr/86%WC球閥、吸紙輥等JK135850(HV)25%（80%Ni/20%Cr）/75%Cr3C2密封環，閥門、汽輪機葉片JK576550(HV)同Stellite6高溫高壓閥門JK6153800(HV)50%WC+50%Deloro 60拉絲塔輪、泵部件粉末硬度化學成分（重量%）典型用途CCrSiWFeMoNiCoMnBNi 25250.203.508.00Bal1.50玻璃模具、各類成型模Ni 35350.3010.503.5010.00Bal2.00玻璃模具、各類成型模Ni 45450.4512.004.0010.00Bal0.102.40排氣閥密封面、柱塞Ni 55550.7515.504.0014.003.00Bal3.00模具、凸輪、柱塞及排閥Ni 60590.8015.504.003.0015.00Bal3.50柱塞、拉絲輥筒、凸輪、機械易損件Ni 62611.0015.503.8014.00BalW:10.54.00造紙機磨盤、鏟車鏟齒Nistelle B冷硬0.101.001.00V:0.35.0028.00Bal2.50高溫耐蝕密封環Deloro 20200.034.502.00Bal0.70玻璃模具、各類成型模等Deloro 22<, SPAN style="FONT, -SIZE: 9pt; FONT-FAMILY: 宋體; COLOR: black; mso-font-kerning: 0pt; mso-bidi-font-family: 宋體">220.200.102.850.50Bal0.501.45玻璃模具、各類成型模Deloro 22M2220.053.002.30Bal0.80玻璃模具、各類成型模等Deloro 28280.050.102.80Bal1.00玻璃模具、各類成型模等Deloro 30300.152.502.601.00Bal0.301.40滑輪、齒輪齒Deloro 35350.204.003.201.400.10Bal0.101.60玻璃模具、閥座Deloro 37360.154.502.60Bal1.00玻璃模具、各類成型模等Deloro 40400.307.503.502.300.10Bal0.101.70螺旋送料器、模芯等,Deloro 50500.4011.004.002.700.10Bal0.102.20泵軸、紙漿刀、閥門、密封環、軸套Deloro60590.6515.004.304.000.10Bal0.103.10擠壓模、螺旋筒體、泵葉、柱塞Deloro6325570.5016.004.003.004.503.00Bal0.103.50耐蝕泵軸、軸套Tribaloy 700540.0815.53.401.5032.50Bal1.50核工業應用抗蝕抗氧化抗輻射粉末硬度化學成分（重量%）典型用途CCrSiWFeMoNiCoMnBHK1582.51025Bal102.5離心澆注用粉HK3581104463Bal103.5離心澆注用粉HK5638.5522.5Bal112.5離心澆注用粉HK761222.55.5Bal3離心澆注用粉NiCo5621194646Bal102.5離心澆注用粉NiCo10560.583.54Bal
焊條牌號型號主要用途硬度HS101～用于堆焊要求耐磨損、抗氧化或耐氣蝕的場合，如鏟斗齒、泵套、柴油機的汽門、排氣葉片等。HRC≥48-54HS111RCoCr-A用于要求在高溫工作時能保持良好的耐磨性及耐蝕性，如高溫、高壓閥門、熱剪切刀刃、熱鍛模等HRC≥40-45HS112RCoCr-B用于高溫、高壓閥門、內燃機閥、高壓泵軸套和內襯套筒、熱軋輥孔型等堆焊HRC≥40-45HS113～用于牙輪鉆頭軸承、鍋爐的旋轉葉片、粉碎機刃口、螺旋送料機等堆焊HRC≥55-60HS113G～用于泵的套筒和旋轉密封環、磨損面板、軸承套筒、高溫熱軋輥、油田鉆頭等堆焊HRC≥54HS113Ni～用于耐氣蝕、耐腐蝕性能要求較高的內燃機氣門、排氣閥的堆焊HRC≥37-40 HS114RCoCr-C用于耐氣蝕、耐腐蝕性能要求較高的內燃機氣門、排氣閥的堆焊HRC≥52HS115RCoCr-E該焊絲是用鉬強化的低碳鈷鉻合金，在室溫下硬度較低，但冷作后硬度有所提高。堆焊層具有良好的耐高溫腐蝕，耐沖擊能和良好的高溫強度HRC≥27HS116RCoCr-C有較高的耐磨損性和高溫強度，但韌性較差，在耐硫酸、磷酸、硝酸等工況條件下呈優良的耐腐蝕性。主要用于銅基及鋁基合金的熱壓模等堆焊HRC≥46-50HS117～有較強的耐磨料磨損及耐腐蝕性能，在800℃高溫也能保持這些特性。用于泵的套筒和旋轉密封環等磨損面的堆焊HRC≥53
D802鈷基堆焊焊條 型號：EDCoCr-A-03 說明：鈷鉻鎢合金焊芯的鈷基堆焊焊條，采用直流反接，堆焊金屬在650℃工作仍能保持良好的耐磨性和耐腐蝕性。 用途：用于在650℃左右工作仍能保持良好的耐磨性和耐腐蝕性的場合，或承受沖擊和冷熱交錯的部位，如堆焊高溫高壓閥門及熱剪刀刃等。 熔敷金屬化學成分/% C 0.7-1.44 Si≤2 Mn≤2 Cr 25-32 Fe≤4 W 3-6 其他≤4 余量為Co堆焊硬度HRC：≥40 D812鈷基堆焊焊條 型號：EDCoCr-B-03 說明：鈷鉻鎢合金焊芯的鈷基堆焊焊條，采用直流反接，堆焊金屬在650℃工作仍能保持良好的耐磨性和耐腐蝕性。 用途：用于高溫高壓閥門、高壓泵的軸套筒和內襯套以及化纖設備的斬刀刃口等。熔敷金屬化學成分/% C 1-1.7 Si≤2 Mn≤2 Cr 25-32 Fe≤5 W 7-10 其他≤4 余量為Co 堆焊硬度HRC：≥44 D822鈷基堆焊焊條 型號：EDCoCr-C-03 說明：高碳鈷鉻鎢合金焊芯的鈷基堆焊焊條，采用直流反接，渣覆蓋性好，成形美觀，具有優良的耐磨、耐熱、耐腐蝕性，在650℃高溫也能保持這些特性。 用途：用于牙輪鉆頭軸承、鍋爐的旋轉葉輪、粉碎機刃口、螺旋送料機等磨損部件的堆焊。 熔敷金屬化學成分/% C 1.75-3 Si≤2 Mn≤2 Cr 25-33 Fe≤5 W 11-19 其他≤4 余量為Co堆焊硬度HRC：≥53 D842鈷基堆焊焊條 型號：EDCoCr-D-03 說明：鈷基4號低碳鈷基鉻鎢合金焊芯堆焊焊條，采用直流反接，堆焊金屬在800℃仍能保持良好的抗熱疲勞性和耐蝕性。 用途：用于高溫條件下承受沖擊和冷熱交錯的工件堆焊，如熱鍛模，閥門密封面等，具有良好的性能。 熔敷金屬化學成分/% C 0.5-0.5 Si≤2 Mn≤2 Cr 23-32 Fe≤5 W≤9.5 其他≤7 余量為Co堆焊硬度HRC：28-35 D852鈷基堆焊焊條 型號：EDCoCr-E-04 說明：用于耐高溫磨損堆焊焊條,工作溫度1100℃,具有紅硬性,抗烈性.也可用于高溫,高壓閥門熱段模等,同時經受沖擊和高溫,耐蝕的部件. HRC≥44 D862鈷基堆焊焊條 型號：EDCoCr-E-05 說明：適用于高溫磨性磨損及細顆粒小角度沖蝕磨損工況。單層堆焊即可滿足性能要求，**工作溫度1000℃,堆焊層硬度：20℃--HRC:64-66、工作溫度600℃--HRC：48-52、工作溫度800℃--HRC：38-42典型應用領域、工況及部分，煉鐵、煉焦、燒潔、水泥等工作領域存在高溫磨損的機械設備。 用途：用于堆焊高溫工件下服役的燒潔單輥破碎機齒冠篦板及高爐旋轉布料溜槽，耐磨效果顯著